在pH为10～12的条件下,先用亚铁离子和钙离子共同沉淀氯化钾镉钴合金电镀和钝化混合废水中的氨三乙酸等羧酸配位剂,六价铬被亚铁离子还原成三价铬后与镉离子、钴离子等一同生成氢氧化物沉淀。再用二甲基二硫代氨基甲酸钠沉淀废水中残留的重金属离子,使其沉淀完全。最后用次氯酸钠氧化废水中的电镀添加剂,降低其化学需氧量(COD)。该方法成本低,处理结果可满足GB 21900–2008《电镀污染物排放标准》的"表3"要求。
Abstract：Ferrous and calcium ions were used to precipitate the carboxylic acid coordinators such as nitrilotriacetic acid in the wastewater discharged from potassium chloride Cd–Co alloy electroplating and passivation at a pH of 10 to 12, during which the hexavalent chromium was reduced to trivalent chromium by ferrous ion and then precipitated with cadmium and cobalt as hydroxides. Sodium dimethyl dithiocarbamate was used to precipitate completely the residual heavy metal ions in the wastewater, and then sodium hypochlorite was used to oxidize the electroplating additives in the wastewater and reduce its chemical oxygen demand(COD). This method is cost-efficient and compliant with the Table 3 in the Emission Standard of Pollutants for Electroplating(GB 21900–2008).
[1]广州超邦化工有限公司.一种氯化钾镉钴合金镀液、其制备方法和电镀工艺:201910526244.6[P]. 2019–08–02.GUO C W, LI X Y, CHEN K, et al. Potassium-chloride cadmium–cobalt alloy plating solution and preparation method and electroplating process thereof:CN110079842A[P]. 2019–08–02.
[2]郭崇武,代朋民.螯合沉淀法去除氯化钾无氰镀镉废水中的镉离子[J].电镀与涂饰, 2018, 37(4):190-192.GUO C W, DAI P M. Removal of cadmium ions from wastewater discharged from cyanide-free potassium chloride cadmium electroplating by chelation precipitation[J]. Electroplating&Finishing, 2018, 37(4):190-192.
[3]郭崇武.漂水和双氧水组合处理含氰废水方法研究[J].电镀与精饰,2006, 28(6):38-40.GUO C W. Investigation of bleaching water&hydrogen peroxide combined treatment method for cyanide-containing waste water[J].Plating&Finishing, 2006, 28(6):38-40.
[4]郭崇武,李健强.用石灰处理电镀含酸废水的方法[J].电镀与精饰,2007, 29(3):48-51.GUO C W, LI J Q. Method for treating electroplating wastewater containing acid using lime[J]. Plating&Finishing, 2007, 29(3):48-51.
[5]郭崇武,李健强.电镀废水处理技术与实践[J].电镀与环保, 2012,32(4):49-53.GUO C W, LI J Q. Technology and practice for electroplating wastewater treatment[J]. Electroplating&Pollution Control, 2012, 32(4):49-53.
[6]郭崇武,李健强,田华.用反渗透技术回收镀镍漂洗水[J].电镀与精饰, 2009, 31(2):40-42.GUO C W, LI J Q, TIAN H. Recovery of nickel-plating rinsing water with reverse osmosis technology[J]. Plating&Finishing, 2009, 31(2):40-42.
[7]郭崇武,赖奂汶,陈康.氧化-螯合沉淀法处理碱性锌镍合金电镀废水[J].电镀与涂饰, 2018, 37(3):137-141.GUO C W, LAI H W, CHEN K. Oxidation–chelation precipitation method for treatment of alkaline zinc-nickel alloy electroplating wastewater[J]. Electroplating&Finishing, 2018, 37(3):137-141.
[8]李小花,郭崇武,吴梅娟.基于沉淀法的化学镀镍废水处理工艺[J].电镀与涂饰, 2018, 37(24):1151-1154.LI X H, GUO C W, WU M J. Process for treatment of the wastewater discharged from electroless nickel plating production based on chelating precipitation[J]. Electroplating&Finishing, 2018, 37(24):1151-1154.
[9]广州超邦化工有限公司.氯化钾无氰镀镉和钝化混合废水的处理方法:201810872068.7[P]. 2020–02–14.GUO C W, LI X H, LAI H W. Potassium chloride cyanide-free cadmium plating and passivation mixed wastewater treatment method:CN110790418A[P]. 2020–02–14.
[10]张允诚,胡如南,向荣.电镀手册[M]. 3版.北京:国防工业出版社,2007:1132.ZHANG Y C, HU R N, XIANG R. Electroplating Handbook[M]. 3rd ed.Beijing:National Defense Industry Press, 2007:1132.
基本信息:
DOI：10.19289/j.1004-227x.2021.02.006
中图分类号:X781.1
引用信息:
[1]郭崇武,陈康.氯化钾镉钴合金电镀废水的组合处理方法[J].电镀与涂饰,2021,40(02):115-118.DOI:10.19289/j.1004-227x.2021.02.006.
2021-01-30
2021-01-30